Structural and hyperfine comparative study of ball-milled and arc-melted Fe50 Cr50 alloys

Autores

  • Germán Yovanny Vélez Universidad del Valle

Palavras-chave:

Stoichiometric alloy, Physics

Resumo

In this work we make a structural and hyperfine comparative study of the Fe50 Cr50 stoichiometric alloy obtained for two different techniques, mechanical alloying and arc-melting. Both alloys were heated to 650 ? C for 7 days, quenched into ice water and then mechanically alloyed for different milling times. Before heat treatment the two alloys exhibit Fe-Cr BCC structure and ferromagnetic behavior similar, after treatment, in the alloy obtained by mechanical alloying, the BCC structure is completely transformed into the ordered structure ? Fe-Cr, whereas that in the alloy obtained by melted this transformation is partial. The mechanical alloying realized in the last stage affect notoriously the structure ? Fe-Cr, for 2 hours of milling the structure is completely disordered, subsequently transformed into BCC Fe-Cr phase, and disappears at 16 hours of milling.

Downloads

Não há dados estatísticos.

Biografia do Autor

Germán Yovanny Vélez , Universidad del Valle

Universidad del Valle

Downloads

Como Citar

VÉLEZ , Germán Yovanny. Structural and hyperfine comparative study of ball-milled and arc-melted Fe50 Cr50 alloys . Physicae Proceedings, Campinas, SP, v. 1, n. 1, p. 1–1, 2020. Disponível em: https://econtents.bc.unicamp.br/eventos/index.php/phyproceedings/article/view/3244. Acesso em: 29 mar. 2024.